Nanomaterials by Mechanical AlloyingNo Access

DENSIFICATION AND GRAIN GROWTH OF NANOCRYSTALLINE NIAL POWDER DURING PRESSURELESS SINTERING

A. MASHREGHY

Materials Science and Engineering Department, School of Engineering, Shiraz University, Shiraz, Iran

Search for more papers by this author

and

M. M. MOSHKSAR

Materials Science and Engineering Department, School of Engineering, Shiraz University, Shiraz, Iran

Search for more papers by this author

https://doi.org/10.1142/S0217979208047730Cited by:3 (Source: Crossref)

Abstract

Nanocrystalline NiAl powder was prepared by mechanical alloying. The prepared powder was cold compacted and sintered at different temperatures and times. The crystallite size of green and sintered compacts was estimated from X-Ray Diffraction peak profile analysis. Thereafter, the Generalized Parabolic Grain Growth model and Master Sintering Curve concept based on Combined Stage Sintering model were employed to investigate the grain growth and densification behavior of nanocrystalline NiAl powder during sintering, respectively. The results of modeling were in a very good agreement to that of experiment. Finally, by comparing the modeling results the sintering parameters were optimized.

Keywords:

You currently do not have access to the full text article.
Recommend the journal to your library today!

References

M. Albiteret al., Materials Science and Engineering A 347, 154 (2003), DOI: 10.1016/S0921-5093(02)00563-4. Crossref, Web of Science, Google Scholar
T. Chen, J. M. Hampikian and N. N. Thadhani, Acta Materialia 47, 2567 (1999), DOI: 10.1016/S1359-6454(99)00059-2. Crossref, Web of Science, ADS, Google Scholar
M. S. Choudry, M. Dollar and J. A. Eastman, Materials Science and Engineering A 256, 25 (1998), DOI: 10.1016/S0921-5093(98)00810-7. Crossref, Web of Science, Google Scholar
J. Joardar, S. K. Pabi and B. S. Murty, Journal of Alloys and Compounds 429, 204 (2007), DOI: 10.1016/j.jallcom.2006.04.045. Crossref, Web of Science, Google Scholar
M. M. Moshksar and M. Mirzaee, Intermetallics 12, 1361 (2004), DOI: 10.1016/j.intermet.2004.03.018. Crossref, Web of Science, Google Scholar
T. R. Smith, Synthesis and Mechanical Properties of Nano-Scale NiAl and NiAl/Al2O3Composites, Mater. Res. Soc. Symp. Proc. 350 (1994) pp. 219–224. Google Scholar
M. M. Moshksar, H. Doty and R. Abbaschian, Intermetallics 5, 393 (1997), DOI: 10.1016/S0966-9795(97)00006-X. Crossref, Web of Science, Google Scholar
Su and D. L. Johnson, Journal of American Ceramics Society 79, 3211 (1996), DOI: 10.1111/j.1151-2916.1996.tb08097.x. Crossref, Web of Science, Google Scholar
D. Hansenet al., Journal of American Ceramics Society 75, 1129 (1992), DOI: 10.1111/j.1151-2916.1992.tb05549.x. Crossref, Web of Science, Google Scholar
O. Yevtushenko, H. Natter and R. Hempelmann, Thin Solid Films 515, 353 (2006), DOI: 10.1016/j.tsf.2005.12.098. Crossref, Web of Science, ADS, Google Scholar
P. Garg, S. J. Park and R. M. German, International Journal of Refractory Metals and Hard Materials 25, 16 (2007), DOI: 10.1016/j.ijrmhm.2005.10.014. Crossref, Web of Science, Google Scholar
D. C. Blaineet al., Metallurgical and Materials Transactions A 37, 2827 (2006), DOI: 10.1007/BF02586115. Crossref, Web of Science, Google Scholar
R. D. Noebe, R. R. Bowman and M. V. Nathal, International Materials Reviews 38, 193 (1993). Crossref, Web of Science, ADS, Google Scholar