Partially aligned and oriented polyacrylonitrile(PAN)-based nanofibers were electrospun from PAN and SWNTs/PAN in the solution of dimethylformamide(DMF) to make the carbon nanofibers. The as-spun nanofibers were hot-stretched in an oven to enhance its orientation and crystallinity. Then it were stabilized at 250 °C under a stretched stress, and carbonized at 1000 °C in N₂ atmosphere by fixing the length of the stabilized nanofiber to convert them into carbon nanofibers. With this hot-stretched process and with the introduction of SWNTs, the mechanical properties will be enhanced correspondingly. The crystallinity of the stretched fibers confirmed by X-ray diffraction has also increased. For PAN nanofibers, the improved fiber alignment and crystallinity resulted in the increased mechanical properties, such as the modulus and tensile strength of the nanofibers. It was concluded that the hot-stretched nanofiber and the SWNTs/PAN nanofibers can be used as a potential precursor to produce high-performance carbon composites.

Keywords:

You currently do not have access to the full text article.
Recommend the journal to your library today!

References

E. Hammelet al., Carbon 42, 1153 (2004), DOI: 10.1016/j.carbon.2003.12.043. Crossref, Web of Science, Google Scholar
H. Q. Houet al., Chem. Mater. 17, 967 (2005), DOI: 10.1021/cm0484955. Crossref, Web of Science, Google Scholar
J. J. Geet al., J. Am. Chem. Soc. 126, 15754 (2004), DOI: 10.1021/ja048648p. Crossref, Web of Science, Google Scholar
S. Chand, J. Mater. Sci. 35, 1303 (2000), DOI: 10.1023/A:1004780301489. Crossref, Web of Science, ADS, Google Scholar
J. T. McCann, M. Marquez and Y. Xia, J. Am. Chem. Soc. 128, 1436 (2006), DOI: 10.1021/ja056810y. Crossref, Web of Science, Google Scholar
Y. Droret al., Langmuir 19, 7012 (2003), DOI: 10.1021/la034234i. Crossref, Web of Science, Google Scholar
S. Maensiri and W. Nuansing, Mater. Chem. Phys. 99, 104 (2006), DOI: 10.1016/j.matchemphys.2005.10.004. Crossref, Web of Science, Google Scholar
W. Watt and B. V. Perov , Handbook of Composites ( Amsterdam, HOLAND , 1985 ) . Google Scholar
W. Ericet al., Proc. of SPIE 6036, 603607-4 (2006). Google Scholar
J. Johnson, L. N. Phillips and W. Watt, Brit Patent 1,110,790 (1965) . Google Scholar
J. Johnson, W. Watt, L. N. Phillips, R. Moreton, Brit Patent 1,166,251 (1966) . Google Scholar
W. H. Norman, W. H. Cheetham and L. Tao, Carbohydrate Polymers 36, 277 (1998). Web of Science, Google Scholar
C. P. Lafrance, M. Pezolet and R. E. Prud'homme, Macromolecules 24, 4948 (1991), DOI: 10.1021/ma00017a035. Crossref, Web of Science, ADS, Google Scholar
S. F. Fennessey and R. J. Farris, Polymer 45, 4217 (2004), DOI: 10.1016/j.polymer.2004.04.001. Crossref, Web of Science, Google Scholar