ELECTRODEPOSITED GRAPHENE OXIDE-HYDROXYAPATITE COMPOSITE COATING WITH IMPROVED BONDING STRENGTH FOR BIOMEDICAL APPLICATION

XIAOQIANG LIU

Qiyuan Pharmaceutical Company Limited, Wangyuan Industrial Park, Yinchuan City 750101, Ningxia Province, P. R. China

https://doi.org/10.1142/S0218625X23500312Cited by:0 (Source: Crossref)

Abstract

In order to improve the interfacial bonding at coating-substrate, a graphene oxide-hydroxyapatite (GH) coating was designed and constructed. The microstructure, bonding strength and in vitro bioactivity of the coating were analyzed. The results showed that GH coating presented uniform and crack-free structure with a flake morphology. The bonding strength of GH coating was 7.81MPa, which is about 1.2 times that of pure hydroxyapatite coating. In vitro bioactivity test using simulated body fluid exhibited that GH coating processes the ability to induce apatite formation. The GH coating should have potential application in surface modification for biomedical materials.

Keywords:

References

1. T. Iwamoto, Y. Hieda and Y. Kogai, Mater. Sci. Eng. C 69 (2016) 1263–1267. Crossref, Web of Science, Google Scholar
2. T. Sahraoui, F. Chouia, Y. I. Bourezg and A. Guelil, Mater. Chem. Phys. 292 (2022) 126865. Crossref, Web of Science, Google Scholar
3. A. Galotta, F. Agostinacchio, A. Motta, S. Dirè, V. M. Sglavo, J. Eur. Ceram. Soc. 43 (2023) 639. Crossref, Web of Science, Google Scholar
4. A. Fomin, M. Fomina, V. Koshuro, I. Rodionov, A. Zakharevich and A. Skaptsov, Ceram. Int. 43 (2017) 11189. Crossref, Web of Science, Google Scholar
5. M. You, L. Zhang, T. A. Gmür, K. Zhang, S. Zürcher, W. Li, G. Yuan, N. D. Spencer and J. Pei, Appl. Surf. Sci. 606 (2022) 154836. Crossref, Web of Science, Google Scholar
6. Q. UlAin, A. N. Khan, M. Nabavinia and M. Mujahid, Mater. Sci. Eng. C 75 (2017) 807. Crossref, Web of Science, Google Scholar
7. C. R. Gautam, S. Kumar, V. K. Mishra and S. Biradar, Ceram. Int. 43 (2017) 14114. Crossref, Web of Science, Google Scholar
8. Z. Li, S. Bi, B. C. Thompson, R. Li and K. A. Khor, Ceram. Int. 43 (2017) 16084. Crossref, Web of Science, Google Scholar
9. L. Ming, X. Pan, Y. Feng, L. S. R. Changhong, Y. Zhichen, L. Ang, L. Huafang, J. Xunming and Z. Yufeng, Bioactive Mater. 3 (2018) 1. Crossref, Web of Science, Google Scholar
10. A. Daniel and V.-R. Maria, J. Mater. Chem. B 8 (2020) 1781. Crossref, Web of Science, Google Scholar
11. K. Dongxu, A. Vu Ashley, B. Amit and B. Susmita, Acta Biomater. 84 (2019) 414. Crossref, Web of Science, Google Scholar
12. Y. Eren, C. Bekir, G. Azim, F. Fehim, G. H. Ozkan, G. Nagihan, M. Ozal and O. Mahmut, Mater. Sci. Eng. C 101 (2019) 292. Crossref, Web of Science, Google Scholar
13. H. Zhao, H. Xing, Q. Lai, Y. Zhao, Q. Chen and B. Zou, Mater. Des. 223 (2022) 111231. Crossref, Web of Science, Google Scholar
14. P. C. S. Boyapati, K. Srinivas and S. Akhil, Mater. Lett. 327 (2022) 133059. Crossref, Web of Science, Google Scholar
15. L. X. Zhang, Z. Sun, J. L. Qi, J. M. Shi, T. D. Hao and J. C. Feng, Carbon 103 (2016) 339. Crossref, Web of Science, Google Scholar
16. L. Long-Hao, K. Young-Min, K. Hae-Won, K. Young-Woon, K. Hyoun-Ee, H. Seong-Joo and K. Jai-Young, Biomaterials 25 (2004) 2867. Crossref, Web of Science, Google Scholar
17. Z. Yanqiang, L. Kezhi, L. Hejun, W. Chuang and L. Hao, Mater. Chem. Phys. 106 (2007) 22. Crossref, Web of Science, Google Scholar
18. Y. Yajing, D. Qiongqiong, H. Yong, H. Shuguang and P. Xiaofeng, Appl. Surf. Sci. 305 (2014) 77. Crossref, Web of Science, ADS, Google Scholar
19. H. Yong, D. Qingqiong, H. Shuguang, Y. Yajing and P. Xiaofeng, J. Mater. Sci. Mater. Med. 24 (2013) 1853. Crossref, Web of Science, Google Scholar
20. J. A. Erakovic, S. M. Miodrag, Z. Matic Ivana, D. J. Zorica, G. C. P. Tsui, T. Chak-yin, M.-S. Vesna, R. K. Yop and P. S. Jin, J. Alloys Compd. 624 (2015) 148. Crossref, Web of Science, Google Scholar