Effect of process parameters on the microstructure evolution of laser surface quenched Ni-Al bronze
Abstract
Laser surface quenching technology was used to modify the surface microstructure of as-cast Ni-Al bronze (NAB). The modified microstructure was studied by scanning electron microscopy (SEM), and the effect of laser process parameters on microstructure evolution was investigated. It was found that a fine-grained zone with fully β phase microstructure formed on the surface of NAB. The depth of the fine-grained zone increased with the increase of laser power, and surface melting occurred when the power reached a threshold value. Laser scanning at a low rate caused the coarsening of grain boundary, while too high rate led to incomplete quenching. Spot overlap ratio determined the microstructure of the superimposed area, and unsuitable ratio would cause bulky κ precipitation at the grain boundary or incomplete transformation from α phase to β phase.