Thermophysical and structural properties of manganese ferrite nanoparticles

Azerbaijan National Academy of Sciences, Institute of Physics, 131 H. Javid Ave., Baku AZ 1143, Azerbaijan

Azerbaijan National Aviation Academy, 30 Mardakan Ave., Baku AZ 1045, Azerbaijan

E-mail Address: aynuragochuyeva@gmail.com

https://doi.org/10.1142/S0217984921505424Cited by:6 (Source: Crossref)

Abstract

This paper discusses the results of the research carried out to study the structure, optical properties and thermophysical properties of a sample (nanopowder with a true density of 4.96 g/cm³, a particle size of 60 nm and a purity of 98.5%, SkySpring Nanomaterials, USA) with high purity. Based on the results of X-ray diffraction, the crystalline phase of MnFe₂O₄ ferrite nanoparticles was completely obtained and the values of the lattice parameters were determined. The results of the MID-IR analysis showed that the absorption coefficient $(α)$ $(α)$ reaches its maximum value at 748 cm $^{- 1}$ $^{- 1}$ wave number. The optical properties of the as-prepared nanostructures were also investigated by VERTEX 70 V diffuse reflectance spectroscopy (DRS). As can be seen from the results of the DSC analysis, the effects occurring in the temperature range up to $30 0^{\circ}$ $30 0^{\circ}$ C clearly reflect the nature of the phase transitions and the amount of energy generated in the ferrite samples.

Keywords:

References

1. M. Y. Rafique et al., Chin. Phys. B 22(10) (2013) 107101. Crossref, Web of Science, Google Scholar
2. N. M. Deraz et al., Int. J. Electrochem. Sci. 7 (2012) 5534. Crossref, Web of Science, Google Scholar
3. D. Carta et al., Phys. Chem. Chem. Phys. 12 (2010) 5074. Crossref, Web of Science, Google Scholar
4. T. Zak et al., Sci. Sinter. 44 (2012) 103. Crossref, Web of Science, Google Scholar
5. S. Sam et al., Int. J. Appl. Sci. Eng. 9(4) (2011) 223. Google Scholar
6. W. H. Kwon et al., J. Magn. 15(4) (2010) 159. Crossref, Web of Science, Google Scholar
7. Z. Z. Lazarevic et al., Acta Phys. Pol. A 121(3) (2012) 682. Crossref, Web of Science, ADS, Google Scholar
8. A. Scano et al., J. Nanopart. Res. 13 (2011) 3063. Crossref, Web of Science, Google Scholar
9. G. Gnanaprakash et al., Mater. Lett. 61 (2007) 4545. Crossref, Web of Science, Google Scholar
10. M. Akhtar et al., J. Nanosci. Nanotechnol. 15 (2015) 9818. Crossref, Web of Science, Google Scholar
11. M. K. Swamy et al., Spectrochim. Acta A, Mol. Biomol. Spectrosc. 151 (2015) 939. Crossref, Web of Science, Google Scholar
12. B. Kozissnik et al., Int. J. Hyperth. 29 (2013) 706. Crossref, Web of Science, Google Scholar
13. K. Krishnan et al., IEEE Trans. Magn. 46 (2010) 2523. Crossref, Web of Science, ADS, Google Scholar
14. S. M. Hussain et al., Toxicol. Sci. 92 (2006) 456. Crossref, Web of Science, Google Scholar
15. S. Kanagesan et al., J. Optoelectron. Biomed. Mater. 6(2) (2014) 41. Google Scholar
16. M. Snoeij et al., IEEE J. Solid State Circuits 51 (2016) 1684. Crossref, Web of Science, ADS, Google Scholar
17. A. N. Hilary et al., Toxicol. Appl. Pharm. 256 (2011) 227. Crossref, Web of Science, Google Scholar
18. S. Elmore, Toxicol. Pathol. 35(4) (2007) 495. Crossref, Web of Science, Google Scholar
19. D. Shi et al., Nanoscale 7 (2015) 8209. Crossref, Web of Science, ADS, Google Scholar
20. D. Toghraie et al., J. Magn. Magn. Mater. 417 (2016) 243. Crossref, Web of Science, ADS, Google Scholar
21. F. Nemec et al., J. Geophys. Res. Space Phys. 121 (2016) 1760. Crossref, Web of Science, ADS, Google Scholar
22. E. Tolman et al., Nucl. Fusion 58 (2018) 046004. Crossref, Web of Science, Google Scholar
23. L. Martinez et al., Sens. Actuators A Phys. 438 (2005) 123. Google Scholar
24. F. Mancoff et al., Appl. Phys. Lett. 77 (2000) 1879. Crossref, Web of Science, ADS, Google Scholar
25. H. Dang et al., Appl. Phys. Lett. 97 (2010) 151110. Crossref, Web of Science, ADS, Google Scholar
26. G. Langfelder et al., IEEE Trans. Magn. 50 (2014) 4700106. Crossref, Web of Science, Google Scholar
27. J. Lenz et al., IEEE Sens. J. 6 (2006) 631. Crossref, Web of Science, ADS, Google Scholar
28. P. Ripka et al., IEEE Sens. J. 10 (2010) 1108. Crossref, Web of Science, ADS, Google Scholar
29. Y. Wang et al., Mater. Today 17 (2014) 269. Crossref, Web of Science, Google Scholar
30. L. Sun et al., Opt. Express 18 (2010) 5407. Crossref, Web of Science, ADS, Google Scholar
31. L. Cheng et al., Opt. Express 21 (2013) 30156. Crossref, Web of Science, ADS, Google Scholar
32. M. Yang et al., Opt. Express 17 (2009) 20777. Crossref, Web of Science, ADS, Google Scholar
33. H. Liu, Sens. Actuators A Phys. 173 (2012) 122. Crossref, Web of Science, Google Scholar
34. G. Ding et al., Appl. Opt. 56 (2017) 4975. Crossref, Web of Science, ADS, Google Scholar
35. J. Chieh et al., Appl. Phys. Lett. 90 (2007) 133505. Crossref, Web of Science, ADS, Google Scholar
36. H. Horng et al., Appl. Phys. Lett. 85 (2004) 5592. Crossref, Web of Science, ADS, Google Scholar
37. E. Tagoudi et al., J. Lightwave Technol. 34 (2016) 5561. Crossref, Web of Science, ADS, Google Scholar
38. A. Candiani et al., Opt. Lett. 36 (2011) 2548. Crossref, Web of Science, ADS, Google Scholar
39. L. Chen et al., Opt. Lett. 36 (2011) 2761. Crossref, Web of Science, ADS, Google Scholar
40. X. Li et al., Opt. Lett. 37 (2012) 5187. Crossref, Web of Science, ADS, Google Scholar
41. D. Jiles et al., J. Magn. Magn. Mater. 61 (1986) 48. Crossref, Web of Science, ADS, Google Scholar
42. M. N. Mirzayev et al., Physica B (2021) 412842. Crossref, Web of Science, Google Scholar
43. M. Tashmetov et al., Int. J. Mod. Phys. B 33 (2019) 1950223. Link, Web of Science, ADS, Google Scholar
44. E. Demir, Mosc. Univ. Phys. Bull. 74(5) (2019) 509. Crossref, Web of Science, ADS, Google Scholar
45. M. N. Mirzayev et al., Pramana J. Phys. 94 (2020) 110. Crossref, Web of Science, ADS, Google Scholar
46. E. P. Popov, A. N. Chernikov, A. I. Beskrovnyi, J. Waliszewski and M. N. Mirzayev, J. Phys., Conf. Ser. 1492 (2020) 012054. Crossref, Google Scholar
47. E. Demir et al., Surf. Rev. Lett. 27(7) (2019) 1950169. Link, Web of Science, ADS, Google Scholar
48. N. Mirzayev et al., Int. J. Mod. Phys. B 34(18) (2020) 2050160. Link, Web of Science, ADS, Google Scholar
49. A. Mary Jacintha et al., J. Nanosci. Nanotechnol. 15 (2015) 9732. Crossref, Web of Science, Google Scholar
50. N. Mirzayev et al., Ceram. Int. 46(3) (2020) 2816. Crossref, Web of Science, Google Scholar
51. N. Mirzayev et al., Mod. Phys. Lett. B (2020) 2050395. Link, Web of Science, Google Scholar
52. N. Mirzayev et al., Rad. Phys. Chem. 180 (2021) 109244. Crossref, Web of Science, Google Scholar
53. E. Demir et al., Vacuum 184 (2021) 109934. Crossref, Web of Science, ADS, Google Scholar
54. M. N. Mirzayev et al., High Temp. 56(3) (2018) 374. Crossref, Web of Science, Google Scholar
55. E. Demir et al., Mod. Phys. Lett. B 33(19) (2019) 1950216. Link, Web of Science, ADS, Google Scholar
56. M. N. Mirzayev et al., Adv. Phys. Res. 1(2) (2019) 63. Google Scholar
57. M. N. Mirzayev et al., J. Alloys Compd. 834 (2020) 155119. Crossref, Web of Science, Google Scholar
58. M. N. Mirzayev, Vacuum 173 (2020) 109162. Crossref, Web of Science, ADS, Google Scholar