Background: This study evaluated the feasibility of using a low-profile titanium (Ti) plate implant, also known as the Ti-button, for Zone II flexor tendon repair. We hypothesize that the use of the Ti-button can distribute the tensile force on the digital flexor tendons to achieve better biomechanical performance.

Methods: Twenty lacerated porcine flexor tendons were randomly divided into two groups and repaired using Ti-button or 6-strand modified Lim-Tsai technique. Ultimate tensile strength, load to 2 mm gap force, and mode of failure were recorded during a single cycle loading test. We also harvested twelve fingers with lacerated flexor digitorum profundus tendons from six fresh-frozen cadaver hands and repaired the tendons using either Ti-button method or modified Lim-Tsai technique. A custom-made bio-friction measurement jig was used to measure the gliding resistance and coefficient of friction of the tendon sheath interface at the A2 pulley.

Results: The ultimate tensile strength, load to 2 mm gap force, stiffness, and gliding resistance of the Ti-button repairs were 101.5 N, 25.7 N, 7.8 N/mm, and 2.2 N respectively. Ti-button repairs had significantly higher ultimate tensile strength and stiffness than the modified Lim-Tsai repair. However, Ti-button also increased the gliding resistance and coefficient of friction but there was no significant difference between the two repair techniques.

Conclusions: Ti-button repair displayed comparable mechanical properties to the traditional repair in terms of 2-mm gap formation and gliding resistance, but with a stronger repair construct. Thus, this deepened our interest to further investigate the potential of using Ti-button implant in Zone II flexor tendon repair by studying both the mechanical and biochemical (tendon healing) properties in more in-depth.

Keywords: