Three types of CFRP/aluminum (Al) alloy riveted joints, single-rivet joint, double-rivet joint and three-rivet joint, were prepared by the riveting technique. The fatigue limit of the three-rivet joint was 27.35 MPa. The fatigue failure mechanism of the joint was that Al alloy cracks on the surface of rivet holes and propagates to fail.

Keywords:

PACS: 62.20.Mk

You currently do not have access to the full text article.
Recommend the journal to your library today!

References

1. J. Limin, Electr. Drive Loco. 4, 1 (2004). Web of Science, Google Scholar
2. H. Zhang and M. Liu, Eng. Plastics Appl. 43, 132 (2015). Google Scholar
3. A. Kelly and R. W. Cahn, Concise Encyclopedia of Composite Materials (Pergamon, 1989), p. 253. Google Scholar
4. Z. De-Gang and C. Gang, Mod. Defence Technol. 46, 24 (2018). Google Scholar
5. F. Rezaei, R. Yunus and N. A. Ibrahim, Mater. Des. 30, 260 (2009). Crossref, Web of Science, Google Scholar
6. F. Lambiase, Mater. Des. 215, 12 (2015). Google Scholar
7. J. Hu et al., Mater. Des. 134, 91 (2017). Crossref, Web of Science, Google Scholar
8. R. Wei et al., Mater. Des. 116, 188 (2017). Crossref, Web of Science, Google Scholar
9. J. Xu, Aviation Technol. 10, 1 (1981). Google Scholar
10. Z. Jie and C. Jilong, Pneumatic Tools Rock Drill. Mach. 2095–6282, 42 (2018). Google Scholar
11. L. Guangyao and F. Xuerui, Forg. Technol. 42, 86 (2017). Web of Science, Google Scholar
12. L. R. Jun, Automobile Technol. 11, 33 (2004). Google Scholar
13. B. Xuechun et al., Mech. Strength 41, 858 (2019). Google Scholar
14. B.-L. Ma et al., J. Zhejiang Univ.-Sci. A 20, 499 (2019). Crossref, Web of Science, Google Scholar
15. W. Ying et al., Light Alloy Process. Technol. 44, 26 (2016). Google Scholar
16. S. Yan, Micro-mechanism research and finite element simulation of fatigue fracture process of high-strength aluminum alloy, Ph.D. Thesis, Yanshan University (2012). Google Scholar