Annealing Temperature Dependence of Various Properties of ZnO Nanoparticles Investigated with Soft XAS
Abstract
In this paper, structural, optical and electronic properties of ZnO nanoparticles were investigated with the variation in the annealing temperature. X-ray diffraction, High-Resolution Transmission Electron Spectroscopy, Absorption spectroscopy, Raman Spectroscopy and Soft X-ray spectroscopy techniques were invoked to investigate and gauge the effect of annealing temperature on these properties. Intact Hexagonal Wurtzite phase of the nanoparticles with increasing crystallinity and spherical shape with particle size between 20nm and 23nm [using both X-ray Diffractometer (XRD) and High-resolution Transmission of electron microscopy (HRTEM)], blue shift of absorption peak from 372nm to 366nm and Optical Band Gap from 3.24eV to 3.17eV (UV-Vis-NIR), narrowing of mode in Raman Spectra; all indicated enhanced crystallinity with increased annealing temperature. Effects produced by the sole variable such as annealing temperature on the indicative parameters in a definite order catapult the annealing conditions as a significant candidate for customized properties. To have a deeper insight at the electronic levels, Synchrotron-based X-ray absorption spectroscopic studies of ZnO nanoparticles were undertaken. The analysis of Soft XAS spectra showed the change in number of O 2 and Zn 4 unoccupied states with increasing particle size and crystallinity of ZnO nanoparticles for varying annealing temperature.
References
- 1. , Rep. Prog. Phys. 72, 126501 (2009). Crossref, Web of Science, Google Scholar
- 2. , J. Alloys Compd. 578, 328 (2013). Crossref, Web of Science, Google Scholar
- 3. , AIP Conf. Proc. 2265, 030130 (2020). Crossref, Google Scholar
- 4. , Appl. Nanosci. 7, 75 (2017). Crossref, Web of Science, Google Scholar
- 5. , IEEE Trans. Electron Dev. 57, 88 (2009). Crossref, Web of Science, Google Scholar
- 6. , Sens. Actuators, A 189, 399 (2013). Crossref, Web of Science, Google Scholar
- 7. , Nano 16, 2150048 (2021). Link, Web of Science, Google Scholar
- 8. , Adv. Funct. Mater. 30, 1907650 (2020). Crossref, Web of Science, Google Scholar
- 9. , Small 13, 1700156 (2017). Crossref, Web of Science, Google Scholar
- 10. , Nano 15, 2050036 (2020). Link, Web of Science, Google Scholar
- 11. , Small 14, 1703754 (2018). Crossref, Web of Science, Google Scholar
- 12. , Adv. Sci. 5, 1700334 (2018). Crossref, Google Scholar
- 13. , Adv. Electron. Mater. 6, 2000168 (2020). Crossref, Web of Science, Google Scholar
- 14. , Optik 127, 4675 (2016). Crossref, Web of Science, Google Scholar
- 15. , J. Alloys Compd. 477, 632 (2009). Crossref, Web of Science, Google Scholar
- 16. , Optik 158, 1006 (2018). Crossref, Web of Science, Google Scholar
- 17. , J. Alloys Compd. 648, 46 (2015). Crossref, Web of Science, Google Scholar
- 18. , Ceram. Int. 37, 393 (2011). Crossref, Web of Science, Google Scholar
- 19. , J. Sci.: Adv. Mater. Devices 2, 51 (2017). Crossref, Web of Science, Google Scholar
- 20. , J. Alloys Compd. 648, 46 (2015). Crossref, Web of Science, Google Scholar
- 21. , Physica B Condens. Matter. 407, 1223 (2012). Crossref, Web of Science, Google Scholar
- 22. , Physica B Condens. Matter. 487, 1 (2016). Crossref, Web of Science, Google Scholar
- 23. , Adv. Mater. Lett. 6, 139 (2015). Crossref, Google Scholar
- 24. , J. Nano Electron. Phys. 5, 02026 (2013). Google Scholar
- 25. , Ceram. Int. 43, 527 (2017). Crossref, Web of Science, Google Scholar
- 26. , J. Mater. Sci.: Mater. Electron. 27, 226 (2016). Crossref, Web of Science, Google Scholar
- 27. , Ceram. Int. 45, 13472 (2019). Crossref, Web of Science, Google Scholar
- 28. , J. Adv. Ceram. 4, 123 (2015). Crossref, Web of Science, Google Scholar
- 29. , Vacuum 179, 109538 (2020). Crossref, Web of Science, Google Scholar
- 30. , J. Alloys Compd. 448, 21 (2008). Crossref, Web of Science, Google Scholar
- 31. , Mater. Res. Express 7, 015079 (2020). Crossref, Web of Science, Google Scholar
- 32. , Mater. Res. Bull. 77, 101 (2016). Crossref, Web of Science, Google Scholar
- 33. , Ceram. Int. 43, 7115 (2017). Crossref, Web of Science, Google Scholar
- 34. , Surf. Sci. 606, L13 (2012). Crossref, Web of Science, Google Scholar
- 35. , Spectrochim. Acta A 81, 53 (2011). Crossref, Web of Science, Google Scholar
- 36. , J. Colloid Interface Sci. 326, 433 (2008). Crossref, Web of Science, Google Scholar
- 37. , Ceram. Int. 45, 1314 (2019). Crossref, Web of Science, Google Scholar
- 38. , J. Appl. Phys. 108, 053904 (2010). Crossref, Web of Science, Google Scholar
- 39. , J. Phys. Conf. Ser. 755, 012040 (2016). Crossref, Google Scholar
- 40. , J. Phys. Chem. C 121, 26076 (2017). Crossref, Web of Science, Google Scholar