The manganese-doped ZnS (ZnS:Mn²⁺) nanocrystals were prepared by addition of Na₂S to an Zinc Oleate and Mn(NO₃)₂ solution. It was done using auto-clave method. The aging in auto-clave resulted in Mn²⁺-doped ZnS particle. The emitting band ZnS:Mn²⁺ showed red-shift from that of ZnS and results in the emission band at 500 nm ~ 650 nm(λ_max = 575 nm). ZnS:Mn²⁺ particles dispersed in polymer for production of the green house films. So this film will be used as light wavelength modification materials for the utilization of plant growth acceleration. Luminescence properties of the film were measured by luminescence spectrometer.

The single crystal growth of KPb₂Br₅ by vertical Bridgman technique using in-house processed zone refined PbBr₂ and KBr with rare-earth terbium doping has been studied. The grown moisture resistant crystals (1.5 cm diameter and 10 cm length) have shown high promise for low phonon energy room temperature solid-state laser applications in the longer side of mid-IR (4-15 μm) due to their high storage lifetimes, wide tunability, and excellent optical quality. The processed crystals are highly transparent (T= ≥80%) in the 0.4-25 μm spectral region. Repeated melting-freezing cycles during differential scanning calorimetry (DSC) experiments did not reveal any appreciable variation in the melting point or phase transitions, which is indicative of their excellent thermal stability. The emission spectra pumped with a 2 μm source show broadband emissions with peak wavelength of 3μm (⁷F₄→ ⁷F₆), 5μm (⁷F₅→ ⁷F₆) and 7.9μm (⁷F₄→ ⁷F₅). The KPb²Br₅:Tb laser crystals will be highly useful for standoff detection of incoming chemical and biological threats using unique infrared absorption signatures.