Narrow Results

Nanostructured zero-valent iron (NSZVI) particles were synthesized by the method of ferric ion reduction with sodium borohydride with subsequent drying and passivation at room temperature in technical grade nitrogen. The obtained sample was characterized by means of X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy and dynamic light scattering studies. The prepared NSZVI particles represent 100–200nm aggregates, which consist of 20–30nm iron nanoparticles in zero-valent oxidation state covered by thin oxide shell. The reactivity of the NSZVI sample, as the removal efficiency of refractory azo dyes, was investigated in this study. Two azo dye compounds, namely, orange G and methyl orange, are commonly detected in waste water of textile production. Experimental variables such as NSZVI dosage, initial dye concentration and solution pH were investigated. The kinetic rates of degradation of both dyes by NSZVI increased with the decrease of solution pH from 10 to 3 and with the increase of NSZVI dosage, but decreased with the increase of initial dye concentration. The removal efficiencies achieved for both orange G and methyl orange were higher than 90% after 80min of treatment.

The potential utility of electrospun polystyrene (PS) nanofibers embedded with 2,6-diiodo-8-phenyl-1,7-dimethyl-3,5-di-2-thienylvinyleneBODIPY for the photocatalytic degradation of azo dyes is investigated. A comparison of the singlet oxygen quantum yield of the $\pi$-extended BODIPY dye in solution and in the PS nanofibers demonstrates that its photosensitizer properties are retained when it is embedded in the solid phase. The photocatalytic degradation properties of the PS nanofibers for Methyl Orange and Orange G were determined by using a Thorlabs 625 nm light emitting diode. The rate of photodegradation increases with the Orange G and Methyl Orange concentration and follows pseudo-first order kinetics at pH 6.7.

The adsorption of three kinds of azo dyes from aqueous solution on HKUST-1/graphene oxide (GO) composite was studied in view of the removal efficiency, adsorption isotherm, and regenerate of the sorbent. HKUST-1/GO was found to be with higher dyes removal efficiency than HKUST-1. All the adsorption isotherms of azo dyes on HKUST-1/GO composite followed Freundlich isotherm. The adsorbed azo dyes on HKUST-1/GO could be eluted by acetone, so HKUST-1/GO can also be used for enrichment of azo dyes as adsorbent.

A composite of chromium (III) terephthalate metal-organic framework and graphene oxide (MIL-101/GO) coated stir bar was prepared by sol–gel technique for the first time and was employed for stir bar sorptive extraction (SBSE) of trace azo dyes amaranth, sunset yellow and carmine from water samples followed by UV–Vis spectrophotometric detection. A MIL-101/GO coating was first created on the glass bar surface. MIL-101/GO and MIL-101/GO coated stir bars were characterized. The enrichment factors of azo dyes by SBSE have been investigated in detail, and the optimized experimental parameters were obtained. Under the optimal conditions, a method for determination of trace amount of azo dyes was setup, and the detection limits of amaranth, sunset yellow and carmine were 2.3 ng/mL, 1.7 ng/mL and 1.6 ng/mL. The proposed method was successfully applied for the analysis of the three azo dyes in water samples.