This study analyzed the relationship between the defect area identified through a C-scan and the void volume in CF-PEKK composite materials through the water absorption behavior to predict the void volume. The water absorption content varies with the defect area; however, the defect area identified through a C-scan and the water absorption content did not show a proportional relationship. This is because voids are distributed in the through-thickness. The results indicated that the absorption behavior could be used to predict the void volume. Irreversible absorption was found to be independent of the void volume. Further, no matrix degradation was seen with water immersion at $70^{\circ }$C; however, some local swelling was seen.

This study analyzed the relationship between the defect area identified through a C-scan and the void volume in CF-PEKK composite materials through the water absorption behavior to predict the void volume. The water absorption content varies with the defect area; however, the defect area identified through a C-scan and the water absorption content did not show a proportional relationship. This is because voids are distributed in the through-thickness. The results indicated that the absorption behavior could be used to predict the void volume. Irreversible absorption was found to be independent of the void volume. Further, no matrix degradation was seen with water immersion at 70^°C; however, some local swelling was seen.